WELDER AND WELDING OPERATOR QUALIFICATION TEST RECORD
WELDING CODE: AWS D1.1
Welders Name: Matthew ODonnell
Company: Accurate Welding Services LLC
Qualification Date: 01/10/21
Welding Process (es) SMAW
Material Spec ASTM A36
Thickness (If pipe, dia. & wall) 3/8" Plate
Type of backing Steel
Identification No. MO 1257
Welders Social Security No. 592-74-1045
Witnessed by: Michael Dobbs
Type Manual
Filler Metal E7018
Filler Wire Diameter 1/8"
Uphill
WELDING PROCEDURE WELDING TECHNIQUES
Single /Multiple Pass: Multiple Amps:100-120 Volts:22-24
Single/Multiple ARC: Single Current: DC Polarity: Reverse
Position of Groove: 4G (Overhead) Inches per Min: 9-12 IPM
REDUCED SECTION TENSILE TEST
Specimen No. Dimensions: Width
Area Ultimate Total Load, LB:
Ultimate Unit Stress, PSI: Character or Failure and Location:
GUIDED BEND TEST
Type and Figure No. 4G Face
Type and Figure No. 4G Root
Type and Figure No.
Type and Figure No.
FILLET TEST RESULTS
Weld Appearance:
Macro Etch Test Results:
Fracture Test Results:
Dimensions: Thickness
Result: Acceptable
Result: Acceptable
Result:
Result:
Fillet Size:
Position:
RADIOGRAPHIC INSPECTION TEST
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
The above WELD o v.rtu of these tests DOES meet welder performance requirements.
Tests Conducted By: Level II Laboratory Test No. NDT4570-IT
NDT NON DESTRUCTIVE
TESTING GROUP
8181 Broadmoor St.
Caledonia, MI. 49316
WELDER AND WELDING OPERATOR QUALIFICATION TEST RECORD
WELDING CODE: AWS D1.1
Welders Name: Matthew ODonnell
Company: Accurate Welding Services LLC
Qualification Date: 01/10/21
Welding Process (es) SMAW
Material Spec ASTM A36
Thickness (If pipe, dia. & wall) 3/8" Plate
Type of backing Steel
Identification No. MO 116
Welders Social Security No. 592-74-1045
Witnessed by: William Spencer
Type Manual
Filler Metal E7018
Filler Wire Diameter 1/8"
Uphill
WELDING PROCEDURE WELDING TECHNIQUES
Single /Multiple Pass: Multiple
Single/Multiple ARC: Single
Position of Groove: 3G (Vertical Uphill)
Specimen No.
Area
Ultimate Unit Stress, PSI:
Type and Figure No.
Type and Figure No.
Type and Figure No.
Type and Figure No.
3G Face
3G Root
Weld Appearance:
Macro Etch Test Results:
Fracture Test Results:
Amps:100-120
Current: DC
Inches per Min: 9-12 IPM
REDUCED SECTION TENSILE TEST
Volts:22-24
Polarity: Reverse
Dimensions: Width Dimensions: Thickness
Ultimate Total Load, LB:
Character or Failure and Location:
GUIDED BEND TEST
FILLET TEST RESULTS
Result: Acceptable
Result: Acceptable
Result:
Result:
Fillet Size:
Position:
RADIOGRAPHIC INSPECTION TEST
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
The above WELD o y virtu of these tests DOES meet welder performance requirements.
Tests Conducted By: Level II Laboratory Test No. NDT1346-1M
NOT NONDESTRUCTIVE
TESTING GROUP
8181 Broadmoor St.
Caledonia, MI. 49316
WELDER AND WELDING OPERATOR QUALIFICATION TEST RECORD
WELDING CODE: AWS D1.1
Welders Name: Joshua Britto
Company: Accurate Welding Services LLC
Qualification Date: 01/10/21
Welding Process (es) SMAW
Material Spec ASTM A36
Thickness (If pipe, dia. & wall) 3/8" Plate
Type of backing Steel
Identification No. JB 115
Welders Social Security No. 590-06-7334
Witnessed by: William Spencer
Type Manual
Filler Metal E7018
Filler Wire Diameter 1/8"
Uphill
WELDING PROCEDURE WELDING TECHNIQUES
Single /Multiple Pass: Multiple Amps:100-120 Volts:22-24
Single/Multiple ARC: Single Current: DC Polarity: Reverse
Position of Groove: 3G (Vertical Uphill) Inches per Min: 9-12 IPM
REDUCED SECTION TENSILE TEST
Specimen No. Dimensions: Width
Area Ultimate Total Load, LB:
Ultimate Unit Stress, PSI: Character or Failure and Location:
Type and Figure No. 3G Face
Type and Figure No. 3G Root
Type and Figure No.
Type and Figure No.
Weld Appearance:
Macro Etch Test Results:
Fracture Test Results:
GUIDED BEND TEST
FILLET TEST RESULTS
Dimensions: Thickness
Result: Acceptable
Result: Acceptable
Result:
Result:
Fillet Size:
Position:
RADIOGRAPHIC INSPECTION TEST
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
The above WELDI%ax y virtue of these tests DOES meet welder performance requirements.
Tests Conducted By: V 'Level II Laboratory Test No. NDT1345-1B
NDW NONDESTRUCTIVE
TESTING GROUP
8181 Broadmoor St.
Caledonia, MI. 49316
WELDER AND WELDING OPERATOR QUALIFICATION TEST RECORD
WELDING CODE: AWS DIA
Welders Name: Joshua Britto
Company: Accurate Welding Services LLC
Qualification Date: 01/10/21
Welding Process (es) SMAW
Material Spec ASTM A36
Thickness (If pipe, dia. & wall) 3/8" Plate
Type of backing Steel
Identification No. JB 1252
Welders Social Security No. 590-06-7334
Witnessed by: Michael Dobbs
Type Manual
Filler Metal E7018
Filler Wire Diameter 1/8"
Uphill
WELDING PROCEDURE WELDING TECHNIQUES
Single /Multiple Pass: Multiple Amps:100-120 Volts:22-24
Single/Multiple ARC: Single Current: DC Polarity: Reverse
Position of Groove: 4G (Overhead) Inches per Min: 9-12 IPM
Specimen No.
Area
Ultimate Unit Stress, PSI:
Type and Figure No.
Type and Figure No.
Type and Figure No.
Type and Figure No.
REDUCED SECTION TENSILE TEST
Dimensions: Width
Ultimate Total Load, LB:
Character or Failure and Location:
GUIDED BEND TEST
Dimensions: Thickness
4G Face Result: Acceptable
4G Root Result: Acceptable
Weld Appearance:
Macro Etch Test Results:
Fracture Test Results:
Result:
Result:
FILLET TEST RESULTS
Fillet Size:
Position:
RADIOGRAPHIC INSPECTION TEST
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
The above WELPM-who—by virtue of these tests DOES meet welder performance requirements.
Tests Conducted By: Level II Laboratory Test No. NDT4565-1B
NIT NON DESTRUCTIVE
TESTING GROUP
8181 Broadmoor St.
Caledonia, MI. 49316
WELDER AND WELDING OPERATOR QUALIFICATION TEST RECORD
WELDING CODE: AWS DIA
Welders Name: William Ledley
Company: Accurate Welding Services LLC
Qualification Date: 01/10/21
Welding Process (es) SMAW
Material Spec ASTM A36
Thickness (If pipe, dia. & wall) 3/8" Plate
Type of backing Steel
Identification No. WL 1242
Welders Social Security No. 262-79-1130
Witnessed by: Michael Dobbs
Type Manual
Filler Metal E7018
Filler Wire Diameter 1/8"
Uphill
WELDING PROCEDURE WELDING TECHNIQUES
Single /Multiple Pass: Multiple Amps:100-120 Volts:22-24
Single/Multiple ARC: Single Current: DC Polarity: Reverse
Position of Groove: 3G (Vertical Uphill) Inches per Min: 9-12 IPM
Specimen No.
Area
Ultimate Unit Stress, PSI:
Type and Figure No. 3G Face
Type and Figure No. 3G Root
Type and Figure No.
Type and Figure No.
Weld Appearance:
Macro Etch Test Results:
Fracture Test Results:
REDUCED SECTION TENSILE TEST
Dimensions: Width
Ultimate Total Load, LB:
Character or Failure and Location:
GUIDED BEND TEST
Dimensions: Thickness
Result: Acceptable
Result: Acceptable
Result:
FILLET TEST RESULTS
Result:
Fillet Size:
Position:
RADIOGRAPHIC INSPECTION TEST
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
The above WELDERo b virtue of these tests DOES meet welder performance requirements.
Tests Conducted By: Level II Laboratory Test No. NDT4555-1L
NOT NON DESTRUCTIVE
TESTING GROUP
8181 Broadmoor St.
Caledonia, MI. 49316
WELDER AND WELDING OPERATOR QUALIFICATION TEST RECORD
WELDING CODE: AWS D1.1
Welders Name: William Ledley
Company: Accurate Welding Services LLC
Qualification Date: 01/10/21
Welding Process (es) SMAW
Material Spec ASTM A36
Thickness (If pipe, dia. & wall) 3/8" Plate
Type of backing Steel
Identification No. WL 1246
Welders Social Security No. 262-79-1130
Witnessed by: Michael Dobbs
Type Manual
Filler Metal E7018
Filler Wire Diameter 1/8"
Uphill
WELDING PROCEDURE WELDING TECHNIQUES
Single /Multiple Pass: Multiple Amps:100-120 Volts:22-24
Single/Multiple ARC: Single Current: DC Polarity: Reverse
Position of Groove: 4G (Overhead) Inches per Min: 9-12 IPM
REDUCED SECTION TENSILE TEST
Specimen No. Dimensions: Width Dimensions: Thickness
Area Ultimate Total Load, LB:
Ultimate Unit Stress, PSI: Character or Failure and Location:
GUIDED BEND TEST
Type and Figure No. 4G Face
Type and Figure No. 4G Root
Type and Figure No.
Type and Figure No.
Weld Appearance:
Macro Etch Test Results:
Fracture Test Results:
Result: Acceptable
Result: Acceptable
Result:
Result:
FILLET TEST RESULTS
Fillet Size:
Position:
RADIOGRAPHIC INSPECTION TEST
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film T.D.
Results:
Remarks:
The above WEL= wh y virtue of these tests DOES meet welder performance requirements.
Tests Conducted By: '-to- Level II Laboratory Test No. NDT4559-2L
NDT NON DESTRUCTIVE
TESTING GROUP
8181 Broadmoor St.
Caledonia, MI. 49316
WELDER AND WELDING OPERATOR QUALIFICATION TEST RECORD
WELDING CODE: AWS D1.1
Welders Name: Raymond VanLuvender Identification No. RV 1249
Company: Accurate Welding Services LLC Welders Social Security No. 038-46-8068
Qualification Date: 01/10/21 Witnessed by: Michael Dobbs
Welding Process (es) SMAW
Material Spec ASTM A36
Thickness (If pipe, dia. & wall) 3/8" Plate
Type of backing Steel
Type Manual
Filler Metal E7018
Filler Wire Diameter 1/8"
Uphill
WELDING PROCEDURE WELDING TECHNIQUES
Single /Multiple Pass: Multiple Amps:100-120 Volts:22-24
Single/Multiple ARC: Single Current: DC Polarity: Reverse
Position of Groove: 3G (Vertical Uphill) Inches per Min: 9-12 IPM
REDUCED SECTION TENSILE TEST
Specimen No. Dimensions: Width Dimensions: Thickness
Area Ultimate Total Load, LB:
Ultimate Unit Stress, PSI: Character or Failure and Location:
GUIDED BEND TEST
Type and Figure No. 3G Face
Type and Figure No. 3G Root
Type and Figure No.
Type and Figure No.
Weld Appearance:
Macro Etch Test Results:
Fracture Test Results:
FILLET TEST RESULT
Result: Acceptable
Result: Acceptable
Result:
Result:
S
Fillet Size:
Position:
RADIOGRAPHIC INSPECTION TEST
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
The above WELD w virtue of these tests DOES meet welder performance requirements.
Tests Conducted By: Level II Laboratory Test No. NDT4562-IV
NOW NONDESTRUCTIVE
TESTING GROUP
8181 Broadmoor St.
Caledonia, MI. 49316
WELDER AND WELDING OPERATOR QUALIFICATION TEST RECORD
WELDING CODE: AWS D1.1
Welders Name: Raymond VanLuvender
Company: Accurate Welding Services LLC
Qualification Date: 01/10/21
Welding Process (es) SMAW
Material Spec ASTM A36
Thickness (If pipe, dia. & wall) 3/8" Plate
Type of backing Steel
Identification No. RV 1250
Welders Social Security No. 038-46-8068
Witnessed by: Michael Dobbs
Type Manual
Filler Metal E7018
Filler Wire Diameter 1/8"
Uphill
WELDING PROCEDURE WELDING TECHNIQUES
Single /Multiple Pass: Multiple Amps:100-120 Volts:22-24
Single/Multiple ARC: Single Current: DC Polarity: Reverse
Position of Groove: 4G (Overhead) Inches per Min: 9-12 IPM
REDUCED SECTION TENSILE TEST
Specimen No. Dimensions: Width Dimensions: Thickness
Area Ultimate Total Load, LB:
Ultimate Unit Stress, PSI: Character or Failure and Location:
GUIDED BEND TEST
Type and Figure No. 4G Face
Type and Figure No. 4G Root
Type and Figure No.
Type and Figure No.
Weld Appearance:
Macro Etch Test Results:
Fracture Test Results:
Result: Acceptable
Result: Acceptable
Result:
Result:
FILLET TEST RESULTS
Fillet Size:
Position:
RADIOGRAPHIC INSPECTION TEST
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
Film I.D.
Results:
Remarks:
The above WELD y virtue of these tests DOES meet welder performance requirements.
Tests Conducted By: evel II Laboratory Test No. NDT4563-1V