Loading...
HomeMy WebLinkAboutACRYLIC SHEETiV SCANNED BY _ St. Lucie County Acrylic Sheet Average Physical Properties of Plexiglas 131 PROPERTY Thickness, nominal Specific gravity Refractive index Light transmittanceand haze "as received" Parallel Total Haze Tensile strength (.25°specimen - 0.2'/min) Maximum Rupture Elongation, maximum Elongation, rupture Modulus of elasticity Poisson's ratio Flexural strength (span depth ratio 16, 0.1'/min Maximum Rupture Deflection, maximum' Deflection, rupture" Modulus of elasticity ASTM Method UNITS in D792 N/A D542 N/A D1003 % D638 psi psi % psi Shear, strength D732 Shear modulus Impact strength Charpy unnotched @73-F D256 bad milled notch @73"F Rockwell Hardness �, a1fi aG Hot forming temperature Deflection temperature under (flexural) load 3.6"F/min-264 psi Maximum recommended continuous service temperature Coefficient of linear thermal expansion 60'F Coefficient of thermal conductivity Specific heat at 77°F Horizontal burning test avd. Burning rate Smoke density Flammability classification Odor Taste .. , D785. D790 psi psi in in psi psi psi ft-lb/ 1/2' x 1' sect. ft-Ib/in. of notch 'F D648 'F 'F R&H P4A iMnr X 105 Cenco-Fitch BTU/(hr)(sq ft)(°FAn) BTU/(Ib)('F) * This valuewillchange with thick- ness. The value given is for the thickness In the column heading. Plexiglas G ' Values reported are averages and 0.236' should not be used for specification 1.19 purposes. For a complete listing of physical 1.49 properties, go to www.plexiglas.com or call your local sales representative 91* and ask for a copy of the Plexiglas 92* General Information and Physical 1* Properties Brochure. 10,500 10,500 4.9 4.9 450,000 0.35 16,000 16,000 0.6 0.6 450,000 9000* 167,000 7.0 0.3 M-100' 290-360 205' 180-200 3.9 1.3 0.35 D635 cm/min 2.8 (in/min) (1.1:') D2843 % 4-10 . _ .. .... _. 94HB. . None None ALTUGLfAS I N T E R N A.T 1 0 N A L ARKEMA GROUP The statements, technical infamtalion and recommendations contained herein are believed to be accurate as of the date hereof. Since the conditions and methods of use of the product and of the informationreferred to herein are beyond our control, Arkema expreressly disclaims any and all liability as to any results obtained oransing from any use of the product or rellance.on such infamialion; NO WARRANTY OF FITNESS FOR ANY PAR. TICULAR PURPOSE. WARBANTY'OF MER. CHANTABILITY OR ANY OTHER WARRANTY, EXPRESS OR IMPLIED. IS MADE CONCERN. ING THE GOODS DESCRIBEDORTHE INFORMATION PROVIDED HEREIN. The information provided herein relates only to the specific Product designated and may not be applicable when wch:pmduct reused in com- binalion with other materials or in any process. The user should thoroughly lest any application before commercialization. Nothing contained herein should be construed as an inducement to infringe any patent. and the user is advised to take appropriate steps to be sure that any proposed use of the product will not result in patent infringement. See MSDS far Health & Safety Consideratinns Altuglas® and.Plexiglas® G are registered trademarks of Arkema. 0 2002 Arkema Inc. AM520120-7ro2cina4h Arkema Inc., 2000 Market Street, Philadelphia, PA 19103 www.altuglasint.com www.Plexiglas.com File C File ©pgY